Method of fabricating discrete nrom cell by self aligned process

ABSTRACT

A method of fabricating discrete NROM cell by self aligned process, comprising the steps of providing a substrate with already formed an ONO layer, wherein the ONO layer includes a top oxide layer, a nitride layer and a bottom oxide layer; defining the top oxide layer; defining a plurality of disposable spacers; implanting a bit line and pocket implant by self-aligned process; defining the nitride layer according to the disposable spacers; defining the bottom oxide layer according to the discrete nitride layer to form a plurality of discrete pillars, so that a channel is formed between two discrete pillars; forming a plurality of channel oxides in the channels; and forming an oxide layer over the discrete channel oxides and the nitrite layer. The method of fabricating discrete NROM cell according to the invention can solve the problem of the electrons being trapped in the nitride layer of NROM cell, and also control the implant and ONO structure at exactly mutual positions.

BACKGROUND OF THE INVENTION

[0001] 1. Field of the Invention

[0002] The invention relates in general to a method of fabricating nitride read-only memory (NROM) cells, and more particularly to the method of fabricating discrete NROM cell by self-aligned process.

[0003] 2. Description of the Related Art

[0004] The memory devices for non-volatile storage of information, such as read only memory (ROM), programmable read only memory (PROM), erasable programmable read only memory (EPROM), and other advanced memory devices, are currently used in the worldwide industries. The other advanced memory devices that involve more complex processing and testing procedures include electrically erasable programmable read only memory (EEPROM), flash EEPROM, and nitride read-only memory (NROM). These advanced memory devices can accomplish the tasks that ROM can't do. For example, using EEPROM devices in circuitry permits in-circuit erasing and reprogramming of the device.

[0005] The main characteristic of NROM is dual bit cells having multiple threshold voltage levels, where every two threshold voltage levels together store a different bit. Others store one bit on either side of the cell. The conventional structures and fabricating methods of NROM cell are described in a lot of articles and references. For example, a dual bit cell of NROM cell is disclosed in U.S. Pat. No. 6,215,148, entitled “NROM cell with improved programming, erasing and cycling”. The process of NROM cell is disclosed in U.S. Pat. No. 6,201,282, entitled “Two bit ROM cell and process for producing same”. The disclosure of the above-identified application is incorporated herein by reference.

[0006]FIG. 1 is a cross-sectional view of a conventional NROM cells. The substrate 10 is implanted a source 12 and a drain 14. The top of substrate 10 lies an sandwiched structure having a nitride layer 17 between a top oxide layer 16 and a bottom oxide layer (tunneling oxide layer) 18, so known as ONO structure. A numbers of BD (buried diffusion) oxide 20 are formed to isolate the adjacent ONO structure and form the channels 22. The structure of NROM cell in which contains dual bit in one cell is also depicted in FIG. 1. The larger region (encircled with the dashed line) denotes a NROM cell 30, and the two smaller regions encircled with the dashed line denote the first bit 32 and the second bit 34.

[0007] In the NROM cell, the nitride layer 17 provides the charge retention mechanism for programming the memory cell. Under normal condition, the electrons are introduced into the nitride layer 17 during reading of the cell, while the holes are introduced into the nitride layer 17 to replace the electrons during un-reading of the cell. Simply saying, the electrons should be able to move between the nitride layer 17 and the implant. However, nitride tends to trap electrons that are introduced in the nitride layer 17 due to its structure. If the electrons are trapped and un-removable, the cell programming function is fade out or the whole cell is even ruined.

[0008] Additionally, according to the hot electron injection phenomenon, some hot electrons will penetrate through the bottom oxide layer 18, especially when it is thin, and then collected in the nitride layer 17. Concentrated charge caused by the hot electrons significantly raises the threshold of the portion of the channel 22 under charge to be higher than the threshold of the remaining portion of the channel 22. When the cell is programmed, the concentrated charge is presented and the raised threshold does not permit the cell to the conductive state. In a normal state, which the concentrated charge is not presented, the reading voltage over the channel can overcome the threshold of the channel 22 and consequently the channel 22 is conducive.

[0009] Moreover, the conventional NROM cell is fabricated by using several steps of photolithography. The implant and the bits are not easily formed at the right position could be shifted, so that the efficiency of the NROM cell is decreased.

SUMMARY OF THE INVENTION

[0010] It is therefore an object of the invention to provide a method of fabricating discrete NROM cell by self-aligned process, so that the problem of electrons trapped in the nitride layer of NROM cell can be solved, and also the mutual positions of the implant and ONO structure can be exactly controlled.

[0011] The invention achieves the above-identified objects by providing a method of fabricating discrete NROM cell by self aligned process, comprising the steps of providing a substrate with already formed an ONO layer, wherein the ONO layer includes a top oxide layer, a nitride layer and a bottom oxide layer; defining the top oxide layer; defining a plurality of disposable spacers; implanting buried bit line and pocket implant by self-aligned process; defining the nitride layer according to the disposable spacers; defining the bottom oxide layer according to the discrete nitride layer to form a plurality of discrete pillars, so that a channel is formed between two discrete pillars; forming a plurality of channel oxides in the channels; and forming an oxide layer over the discrete channel oxides and the nitrite layer.

BRIEF DESCRIPTION OF THE DRAWINGS

[0012] Other objects, features, and advantages of the invention will become apparent from the following detailed description of the preferred but non-limiting embodiments. The description is made with reference to the accompanying drawings in which:

[0013]FIG. 1 (prior art) is a cross-sectional view of a conventional NROM cells;

[0014]FIG. 2A˜FIG. 2M illustrate the method of fabricating discrete NROM cell by self-aligned process according to the first embodiment of the invention; and

[0015]FIG. 3A˜FIG. 3P illustrate the method of fabricating discrete NROM cell by self-aligned process according to the second embodiment of the invention.

DETAILED DESCRIPTION OF THE INVENTION

[0016] Although two methods are taken for examples to illustrate how to fabricate the discrete NROM cell by self-aligned process, the invention is not limited to the disclosed embodiments. Also, to avoid obscuring the invention, well-known elements not directly relevant to the invention are not shown or described. Accordingly, the specification and the drawing are to be regard as an illustrative sense rather than a restrictive sense.

EXAMPLE 1

[0017]FIG. 2A˜FIG. 2M illustrate the method of fabricating discrete NROM cell by self-aligned process according to the first embodiment of the invention. In FIG. 2A, a substrate 210 is provided and a sandwiched structure known as ONO layer is formed thereon. The ONO layer includes a bottom oxide layer (tunneling oxide layer) 218 grown on the substrate 210, a nitride layer 217 deposited over the bottom oxide layer 218, and a top oxide layer 216 produced on the nitride layer 217. Then, photo-resist (PR) is deposited over the top oxide layer 216 and patterned according to the mask (not shown in FIG. 2A) to form a patterned PR 219.

[0018] The thickness of the bottom oxide layer 218 typically ranges from 50 Å to 150 Å, and preferably about 70 Å. The thickness of the nitride layer 217 typically ranges from 20 Å to 150 Å. The thickness of the top oxide layer 216 is not limited since it will be removed in the following procedures. However, it will be appreciated that the thickness of ONO layer are generally independent of each other, and variable depending on the field of NROM cell application.

[0019] Next, the top oxide layer 216 is etched according to the patterned PR 219, as shown in FIG. 2B. The top oxide under the patterned PR 219 remains on while the others not be covered are etched away. Then, the patterned PR 219 is removed as shown in FIG. 2C.

[0020] A disposable film is then formed over the top oxide layer 216 and portion of the nitride layer 217 by conformal deposition. Subsequently, the disposable film is etched by non-conformal etching process, and the disposable spacers 221 are formed on the sides of the discrete top oxide, as shown in FIG. 2D. The disposable film could be any material that can be differentiated from Nitride. For example, using polysilicon as the disposable film can be selectively etched away and makes the etching process easy to be controlled. Also, it is noted that the bottom width of the disposable spacer 221 is controlled at a predetermined value (d).

[0021] As illustrated by FIG. 2E, the buried bit line and pocket implant 222 are implanted by self-aligned process. The buried bit line is phosphorus (P) or arsenic (As), and the pocket implant is boron (B) or BF₂ ⁺. Then, the top oxide layer 216 is etched away by the high selectivity of disposable film (poly) and oxide, as shown in FIG. 2F.

[0022] In FIG. 2G, the nitride layer 217 is etched by the high selectivity of disposable film (poly), nitride and oxide. The nitride sheltered by the disposable spacers 221 remains on the bottom oxide while the other portions not covered by are etched away. Then, the disposable spacers 221 are removed, as shown in FIG. 2H. After that, the bottom oxide 218 is etched according to remaining nitride 217, as shown in FIG. 21.

[0023] As far as the process describe, the nitride layer 217 and the bottom oxide layer 218 have been etched and formed as a plurality of pillars. Between the discrete pillars is a channel. In FIG. 2J, those channels are filled with the oxide 224 by oxidation or by deposition. Then, another oxide layer 226 is formed over the channel oxide 224 and the nitride layer 217, as shown in FIG. 2K. The oxide layer 226 is produced either through oxidation of the nitride, or by deposition or by a combination thereof.

[0024] Following the channel oxidation step, a layer such as a polysilicon layer 228 is formed over the oxide layer 226 as a cap in FIG. 2L. The polysilicon layer can be amorphous polysilicon, or grand polysilicon, or dopant polysilicon. Also, in the particular process, the Tungsten Silicide (WSi_(x)) is subsequently deposited over the polysilicon layer 228 (not shown in FIG. 2L). The polysilicon layer 228 is performed as the electrode, and can be patterned as the word-line.

[0025] The NROM cell is then finished in the aforementioned ways, and the discrete NROM cell of the invention is depicted in FIG. 2M. The larger encircled region denotes a NROM cell 230, and the two smaller encircled regions denote the first bit 232 and the second bit 234. Two bits are in the predetermined width (d). It is noted that the buried bit line and pocket implant is implanted by self-aligned process and the following steps are also performed by self-aligned process. Therefore, the mutual position of the buried bit line and pocket implant 222 and the ONO layer can be easily and exactly controlled.

EXAMPLE 2

[0026]FIG. 3A˜FIG. 3P illustrate the method of fabricating discrete NROM cell by self-aligned process according to the second embodiment of the invention. The fabricating method of Example 2 is mostly the same as that of Example 1, but some of steps are slightly modified or changed in different orders.

[0027] The drawings of FIG. 3A and FIG. 3B are identical with FIG. 2A and FIG. 2B. In FIG. 3A, a substrate 310 is first provided and a ONO structure including a top oxide layer 316, a nitride layer 317, and a bottom oxide layer (tunneling oxide layer) 318 is formed thereon. Then, a patterned photo-resist (PR) 319 is formed over the top oxide layer 316 by photolithography. Similarly, the thickness of three layers of ONO structure are generally independent of each other, and variable depending on the field of NROM cell application. Next, the top oxide layer 316 is etched according to the patterned PR 319, as shown in FIG. 3B.

[0028] After that, the buried bit line and pocket implant 322 are implanted by self-aligned process, as shown in FIG. 3C. The buried bit line is phosphorus (P) or arsenic (As), and the pocket implant is boron (B) or BF₂ ⁺. Then, the patterned PR 319 is descummed for exposing the portion of the top oxide layer 316 at the predetermined width d, as illustrated in FIG. 3D.

[0029] The top oxide layer 316 is then etched according to the PR descum, and followed by removing PR 319, as shown in FIG. 3E and FIG. 3F.

[0030] As illustration of FIG. 3G, a disposable film 320 is then formed over the top oxide layer 316 and the portion of the nitride layer 317 by conformal deposition. Subsequently, the disposable film 320 is etched by non-conformal etching process, and the disposable spacers 321 are formed on the sides of the discrete top oxide layer 316, as shown in FIG. 3H. The disposable film could be any material that can be differentiated from Nitride, such as polysilicon. Also, it is noted that the bottom width of the disposable spacer 321 is controlled at the predetermined value, d.

[0031] Next, the discrete top oxide layer 316 is etched away by the high selectivity of disposable film (poly), nitride and oxide, as shown in FIG. 3I. The nitride layer 317 is then etched according to the disposable spacer 321. The nitride sheltered by the disposable spacers 321 remains on the bottom oxide layer 318 while the other portion not covered by is etched away, as shown in FIG. 3J.

[0032] In FIG. 3K, the disposable spacers 321 are removed. The bottom oxide 318 is then etched according to the remaining nitride, as shown in FIG. 3L. As far as the foregoing steps describe, the nitride layer 317 and the bottom oxide layer 318 have been etched and formed as a plurality of pillars (FIG. 3L). Between the discrete pillars is a channel. In FIG. 3M, those channels are filled with the oxide 324 by oxidation or deposition. Then, another oxide layer 326 is formed over the channel oxide 324 and the nitride layer 317, as shown in FIG. 3N. The oxide layer 326 is produced either through oxidation of the nitride, or by deposition or by a combination thereof.

[0033] Following the oxidation, the oxide layer 326 is capped with a film such as a polysilicon layer 328, as shown in FIG. 30. The polysilicon layer 328 is performed as the electrode, and can be patterned as the word-line.

[0034] The NROM cell is then finished in the aforementioned ways, and the discrete NROM cell of the invention is depicted in FIG. 3P. The larger encircled region denotes a NROM cell 330, and the two smaller encircled regions denote the first bit 332 and the second bit 334. Two bits are in the predetermined width of d. It is noted that the buried bit line and pocket implant is implanted by self-aligned process and the following steps are also performed by self-aligned process. Therefore, the mutual position of the buried bit line and pocket implant 322 and the ONO layer can be easily and exactly controlled.

[0035] The present invention uses self-aligned process to fabricate the NROM memory cell, and the buried bit line implant, pocket implant and dual bit in one cell are exactly formed at the right positions. Also, the bits of the invention are separated by channel oxide so that the problem due to the electrons being trapped in the nitride layer can be solved.

[0036] While the invention has been described by ways of examples and in terms of the preferred embodiments, it is to be understood that the invention is not limited to the disclosed embodiment. To the contrary, it is intended to cover various modifications and similar arrangements and procedures, and the scope of the appended claims therefore should be accorded the broadest interpretation so as to encompass all such modifications and similar arrangements and procedures. 

What is claimed is:
 1. A method of fabricating discrete NROM cell by self aligned process, comprising the steps of: providing a substrate with already formed an ONO layer, wherein the ONO layer includes a top oxide layer, a nitride layer, and a bottom oxide layer; defining the top oxide layer; defining a plurality of disposable spacers; implanting an bit line and pocket implant by self-aligned process; defining the nitride layer according to the disposable spacers; defining the bottom oxide layer according to the discrete nitride layer to form a plurality of discrete pillars, so that a channel is formed between two discrete pillars; forming a plurality of channel oxides in the channels; and forming an oxide layer over the discrete channel oxides and the nitrite layer.
 2. The method of fabricating discrete NROM cell according to claim 1, wherein the step of defining the top oxide layer further comprises the steps of: placing a photoresist on the top oxide layer; placing a mask on the photoresist; etching the top oxide layer; and removing the photoresist.
 3. The method of fabricating discrete NROM cell according to claim 1, wherein the step of defining a disposable spacer further comprises the steps of: forming a disposable film on the top oxide layer by conformal deposition; etching the disposable film by non-conformal etching process; and removing the discrete top oxide layer.
 4. The method of fabricating discrete NROM cell according to claim 3, wherein the disposable film is polysilicon.
 5. The method of fabricating discrete NROM cell according to claim 1, wherein the step of defining the nitride layer further comprises the steps of etching the nitride layer and removing the disposable spacers.
 6. The method of fabricating discrete NROM cell according to claim 1, wherein the oxide layer, formed over the discrete channel oxides and the nitrite layer, is produced either through oxidation of the nitride layer or by deposition or by a combination thereof.
 7. The method of fabricating discrete NROM cell according to claim 1, wherein after the step of forming the oxide layer over the discrete channel oxides and the nitrite layer, the oxide layer is capped with an electrode layer.
 8. The method of fabricating discrete NROM cell according to claim 7, wherein the polymer layer is polysilicon.
 9. The method of fabricating discrete NROM cell according to claim 1, wherein the step of defining the top oxide layer further comprises the steps of: forming a patterned photoresist; descumming the patterned photoresist; etching the top oxide layer according to the descummed patterned photoresist; and removing the photoresist. 